Microstructural analysis of thermally induced and deformation induced martensitic transformations in Fe–12.5 wt.% Mn–5.5 wt.% Si–9 wt.% Cr–3.5 wt.% Ni alloy

01 Ocak 2006 Makale Google Scholar
Yazarlar
PROFESÖR TALİP KIRINDI

Atıf kopyala

P. T. KIRINDI (2006). Microstructural analysis of thermally induced and deformation induced martensitic transformations in Fe–12.5 wt.% Mn–5.5 wt.% Si–9 wt.% Cr–3.5 wt.% Ni alloy. *Journal of alloys and compounds 407 (1-2), 157-162, 2006*.

Yayın bilgileri

Dergi Journal of alloys and compounds 407 (1-2), 157-162, 2006
Veri tabanı Google Scholar
Kaynak GoogleScholar
Yayına Git

Atıf verisi 14 Kasım 2026 tarihinde güncellendi.

T Kirindi, M Dikici | Journal of alloys and compounds 407 (1-2), 157-162, 2006

Kaynak bazlı atıf

Kaynak Atıf
Google Scholar 33
Etkin 0

Yayın metrikleri (GS / WoS / Scopus)

33 Google Scholar Atıf
AI Asistan
Çevrimiçi