Comparison of dry sliding wear behavior and microstructural properties of AISI 8620 steel after gas carburization, gas nitriding, and pack boronization surface treatment

KIRIKKALE ÜNİVERSİTESİ Kariyer
Personel Giriş Giriş

Yayın

Comparison of dry sliding wear behavior and microstructural properties of AISI 8620 steel after gas carburization, gas nitriding, and pack boronization surface treatment

01 Ocak 2026 Makale Google Scholar
Yazarlar
DOÇENT AZİZ BARIŞ BAŞYİĞİT

Atıf kopyala

D. A. B. BAŞYİĞİT (2026). Comparison of dry sliding wear behavior and microstructural properties of AISI 8620 steel after gas carburization, gas nitriding, and pack boronization surface treatment. *Materials Testing 67 (12), 1-13, 2026*.

Yayın bilgileri

Dergi Materials Testing 67 (12), 1-13, 2026
Veri tabanı Google Scholar
Kaynak GoogleScholar
Yayına Git

Atıf verisi 14 Kasım 2026 tarihinde güncellendi.

B A. B, O Sahin, B S. U, K V. | Materials Testing 67 (12), 1-13, 2026

Kaynak bazlı atıf

Kaynak Atıf
Google Scholar 6
Etkin 0

Yayın metrikleri (GS / WoS / Scopus)

6 Google Scholar Atıf
AI Asistan
Çevrimiçi